Welding Suitability

Curious about what we can weld? We will tell you all about it on this page!

Commercially pure aluminium welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Aluminium alloys
  • Copper
  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel
  • Nickel
  • Titanium alloys
  • Tungsten 

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Copper alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Copper welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Copper alloys
  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel
  • Nickel

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Mild steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Nickel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel
  • Martensitic stainless steel 

Generally readily weldable post weld heat treatment recommended;

  • Through hardening steel
  • High speed steel

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys
  • Nickel alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Low alloy steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper

Generally readily weldable may require post weld heat treatment;

  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Nickel 

Generally readily weldable post weld heat treatment recommended;

  • Through hardening steel
  • High speed steel
  • Martensitic stainless steel 

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys 

Weldability varies depending upon alloy may require post weld heat treatment;

  • Nickel alloys

Weldability varies depending upon alloy post weld heat treatment recommended;

High speed steel welded to

Generally readily weldable;

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • High speed steel

Weldability varies depending upon alloy;

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Ferritic stainless steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel
  • Martensitic stainless steel

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys
  • Through hardening steel

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

PH stainless steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel
  • Martensitic stainless steel

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys
  • Through hardening steel

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Nickel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel

Generally readily weldable post weld heat treatment recommended;

  • Through hardening steel

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Niobium welded to

Generally readily weldable;

  • Niobium

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Tungsten welded to

Generally readily weldable;

  • Commercially pure aluminium

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Aluminium alloys welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Aluminium alloys

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Copper
  • Copper alloys
  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel
  • Nickel
  • Tungsten 

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Copper alloys welded to

Generally readily weldable;

  • Copper
  • Copper alloys

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Commercially pure aluminium
  • Aluminium alloys
  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel
  • Nickel

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Medium carbon steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Nickel

Generally readily weldable may require post weld heat treatment;

  • Medium carbon steel
  • Low alloy steel
  • Martensitic stainless steel 

Generally readily weldable post weld heat treatment recommended;

  • Through hardening steel
  • High speed steel

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys 

Weldability varies depending upon alloy may require post weld heat treatment;

  • Nickel alloys

Weldability varies depending upon alloy post weld heat treatment recommended;

Through hardening steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

  • Mild steel
  • Medium carbon steel
  • Low alloy steel
  • Through hardening steel
  • High speed steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel
  • Nickel

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

  • Nickel alloys
Austenitic stainless steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel
  • Martensitic stainless steel

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys
  • Through hardening steel

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Duplex stainless steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper
  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel

Generally readily weldable may require post weld heat treatment;

  • Low alloy steel
  • Martensitic stainless steel

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys
  • Through hardening steel

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Martensitic stainless steel welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Copper

Generally readily weldable may require post weld heat treatment;

  • Mild steel
  • Medium carbon steel
  • Austenitic stainless steel
  • Ferritic stainless steel
  • Duplex stainless steel
  • PH stainless steel
  • Martensitic stainless steel

Generally readily weldable post weld heat treatment recommended;

  • Low alloy steel
  • Through hardening steel

Weldability varies depending upon alloy;

  • Aluminium alloys
  • Copper alloys

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Nickel alloys welded to

Generally readily weldable;

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

  • Mild steel

Weldability varies depending upon alloy may require post weld heat treatment;

  • Medium carbon steel
  • Low alloy steel

Weldability varies depending upon alloy post weld heat treatment recommended;

  • Through hardening steel
Titanium alloys welded to

Generally readily weldable;

  • Commercially pure aluminium
  • Titanium alloys

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;

Zirconium welded to

Generally readily weldable;

  • Zirconium

Generally readily weldable may require post weld heat treatment;

Generally readily weldable post weld heat treatment recommended;

Weldability varies depending upon alloy;

Weldability varies depending upon alloy may require post weld heat treatment;

Weldability varies depending upon alloy post weld heat treatment recommended;